Stabilization of FGD gypsum for its disposal in landfills using amorphous aluminium oxide as a fluoride retention additivehslabrasive.com

The applicability of amorphous aluminium oxide as a fluoride retention additive to flue gas desulphurisation (FGD) gypsum was studied as a way of stabilizing this by-product for its disposal in landfills. Using a batch method the sorption behaviour of amorphous aluminium oxide was evaluated at the pH (about 6.5) and background electrolyte conditions (high chloride and sulphate concentrations) found in FGD gypsum leachates. It was found that fluoride sorption on amorphous aluminium oxide was a very fast process with equilibrium attained within the first half an hour of interaction. The sorption process was well described by the Langmuir model, offering a maximum fluoride sorption capacity of 61.7 mg g(-1). Fluoride sorption was unaffected by chloride co-existing ions, while slightly decreased (about 20%) by competing sulphate ions. The use of amorphous aluminium oxide in the stabilization of FGD gypsum proved to greatly decreased its fluoride leachable content (in the range 5-75% for amorphous aluminium oxide doses of 0.1-2%, as determined by the European standard EN 12457-4 [EN-12457-4 Characterization of waste-leaching-compliance test for leaching of granular waste materials and sludges-Part 4: one stage batch test at a liquid to solid ratio of 10 l/kg for materials with particle size below 10mm (without or with size reduction)]), assuring the characterization of this by-product as a waste acceptable at landfills of non-hazardous wastes according to the Council Decision 2003/33/EC [Council Decision 2003/33/EC of 19 December 2002. Establishing criteria and procedures for the acceptance of waste at landfills pursuant to Article 16 of and Annex II to Directive 1999/31/EC] on landfill of wastes.wholesale Aluminium Oxide Furthermore, as derived from column leaching studies, the proposed stabilization system proved to be highly effective in simulated conditions of disposal, displaying a fluoride leaching reduction value about 81% for an amorphous aluminium oxide added amount of 2%.